細胞形狀作為一個幾何因素可以影響干細胞分化,這是近年來國際學術界一個涉及生物材料、再生醫(yī)學和干細胞命運調(diào)控的重要發(fā)現(xiàn)。我系丁建東課題組在此領域也有獨到研究,相繼發(fā)表多篇文章,如:
? ? ? 1.Rong Peng, Xiang Yao, and Jiandong Ding*, Effect of cell anisotropy on differentiation of stem cells on micropatterned surfaces through the controlled single cell adhesion, Biomaterials, 32, 8048-8057 (2011)
http://www.sciencedirect.com/science/article/pii/S0142961211008064
? ? ? 2.Xiang Yao, Rong Peng, and Jiandong Ding*, Effects of aspect ratios of stem cells on lineage commitments with and without induction media, Biomaterials, 34(4), 930-939 (2013)?
http://www.sciencedirect.com/science/article/pii/S0142961212012033
? ? ? 3.Xiang Yao, Rong Peng, and Jiandong Ding*, Cell-material interactions revealed via material techniques of surface patterning, Adv. Mater., 25(37), 5257-5286 (2013)?
http://onlinelibrary.wiley.com/doi/10.1002/adma.201301762/abstract
? ? ? 4.Bin Cao, Rong Peng, Zhenhua Li, Jiandong Ding*, Effects of spreading areas and aspect ratios of single cells on dedifferentiation of chondrocytes, Biomaterials, 35, 6871-6881 (2014)?
http://www.sciencedirect.com/science/article/pii/S0142961214005201
丁建東課題組近來還報道,細胞器的形狀也可以成為一種影響因素。課題組前期采用微電子技術制備的模板獲得了高分子材料的微柱陣列。在適當?shù)奈㈥嚵谐叨认掠^察到了細胞核的自我形變,這種細胞器的形變并不是細胞整體外形的縮影,具有相對獨立性。隨后的深入研究進一步發(fā)現(xiàn),細胞核變形的半定量程度隨微柱高度呈現(xiàn)類似一級相變的規(guī)律:這種細胞核變形即便在經(jīng)過較長的干細胞誘導分化后依然得以保持。在細胞核的自我形變下,骨髓基質(zhì)干細胞依然保持了成骨誘導和成脂誘導的潛能,但是分化程度則受到了細胞核形狀的影響。這種影響與通常人們在沒有顯著細胞核變形的平整兩維表面情況下的規(guī)律不一致,揭示了細胞核有較為強大的調(diào)控功能。
以劉香男博士生為第一作者的13個印刷頁的全文于2016年10月4號在生物材料權威期刊Biomaterials在線發(fā)表。詳見Subcellular cell geometry on micropillars regulates stem cell differentiation,Xiangnan Liu, Ruili Liu, Bin Cao, Kai Ye, Shiyu Li, Yexin Gu, Zhen Pan, Jiandong Ding*, Biomaterials, 111, 27-39 (2016). 文章鏈接:http://www.sciencedirect.com/science/article/pii/S0142961216305245
?
?